Effect of metal doping into Ce0.5Zr0.5O2 on photocatalytic activity of TiO2/Ce0.45Zr0.45M0.1OX (M=Y, La, Mn)
Bo, Lintao, Maochu, Li, Min, Ming, Chen (2007) Effect of metal doping into Ce0.5Zr0.5O2 on photocatalytic activity of TiO2/Ce0.45Zr0.45M0.1OX (M=Y, La, Mn) J Hazard Mater (IF: 12.2) 143(1-2) 516-21Abstract
The paper demonstrates that the photocatalytic activity of TiO2 towards the decomposition of gaseous benzene in a batch reactor can be greatly improved by loading TiO2 on the surface of CeO(2)-ZrO(2). The research investigates the effects of three metals doping into Ce(0.5)Zr(0.5)O(2) on photocatalytic activity of TiO2/Ce(0.45)Zr(0.45)M(0.1)O(X) (M=Y, La, Mn). The prepared photocatalysts were characterized by BET, XRD, UV-vis diffuse reflectance and XPS analyses. BET surface area of TiO2/Ce(0.45)Zr(0.45)M(0.1)O(X) (M=Y, La, Mn) is smaller than that of Ce(0.5)Zr(0.5)O(2). XRD results reveal that the deposited titania is highly dispersed as in the CeO(2)-ZrO(2) matrix, doping M in the CeO(2)-ZrO(2) lattice causes the changing of lattice space and the diffraction peaks shift to higher 2theta position. Among these four catalysts, the band gap value of TiO(2)/Ce(0.45)Zr(0.45)La(0.1)O(X) is the lowest. The binding energy value of Ti 2p(3/2) of four catalysts transfers to a lower value. The order of photocatalytic activity is TiO2/Ce(0.45)Zr(0.45)La(0.1)O(X)>TiO2/Ce(0.45)Zr(0.45)Y(0.1)O(X)>TiO2/Ce(0.45)Zr(0.45)Mn(0.1)O(X)>TiO2/Ce(0.5)Zr(0.5)O(2)>TiO2. The proposed mechanism is of electron transfer and the stronger absorption in the region 210-400 nm.
Links
http://www.ncbi.nlm.nih.gov/pubmed/17084025http://dx.doi.org/10.1016/j.jhazmat.2006.09.071